Technical Data Sheet
BRADY XB-400 POLYMER COATED CLOTH
TDS No. XB-400
Effective Date: 02/21/2000
Description:
Brady XB-400 is a polymer coated cloth with a matte thermal transfer printable topcoat and a rubber based pressure sensitive adhesive.
XB-400 is a general purpose material for labeling and marking applications requiring a thermal transfer printable surface. XB-400 is a good wire and cable marker material.
XB-400 has good smudge resistance and is resistant to oil, water, and fading. XB-400 has good flexibility for wrapping around curved surfaces.
Recommended ribbon is the Brady Series R4300 black for optimum print performance.
Details:
PHYSICAL PROPERTIES
TEST METHODS
AVERAGE RESULTS
Total Thickness
ASTM D 1000
0.0073 inch (0.185 mm)
Adhesion to:
-Stainless Steel
-Polypropylene
-Textured ABS
ASTM D 1000
20 minute dwell
24 hour dwell
20 minute dwell
24 hour dwell
20 minute dwell
24 hour dwell
80 oz/inch (88 N/100 mm)
91 oz/inch (100 N/100 mm)
71 oz/inch (78 N/100 mm)
86 oz/inch (94 N/100 mm)
38 oz/inch (42 N/100 mm)
38 oz/inch (42 N/100 mm)
Tack
ASTM D 2979
Polyken™ Probe Tack
(1 second dwell, 1 cm/sec separation)
43.9 oz (1350 g)
Application Temperature
Lowest application temperature to stainless steel
40°F (4°C)
Tensile Strength and Elongation
ASTM D 1000
-Machine direction
-Cross direction
50 lbs/inch (876 N/100 mm), 7%
35 lbs/inch (613 N/100 mm), 18%
The following testing is performed with XB-400 printed with Brady Series R4300 ribbon. All samples were allowed to dwell 24 hours prior to testing. Samples were tested on flat aluminum panels and wrapped around 0.080" OD TFE wires.
PERFORMANCE PROPERTIES
TEST METHODS
TYPICAL RESULTS
High Service Temperature
30 days at 175°F (80°C)
Slight topcoat darkening at 80°C
Low Service Temperature
30 days at -40°F (-40°C)
No visible effect
Humidity Resistance
30 days at 100°F (37°C), 95% R.H.
No visible effect
UV Light Resistance
30 days in UV Sunlighter™ 100
No visible effect
< /td>
Weatherability
ASTM G 26
30 days in Xenon Arc Weatherometer
No visible effect
Salt Fog Resistance
ASTM B 117
30 days in 5% salt fog solution chamber
No visible effect
Abrasion Resistance
Taber Abraser, CS-10 grinding wheels, 250 g/arm (Fed. Std. 191A, Method 5306)
Print still legible after 100 cycles
PERFORMANCE PROPERTY
CHEMICAL RESISTANCE
Samples were printed with the R4300 ribbon, laminated to flat aluminum panels and wrapped around 0.080" OD TFE jacketed wire, and allowed to dwell 24 hours prior to test. Testing consisted of 5 cycles of 10 minute immersions in the specified chemicals followed by 30 minute recovery periods. After the final immersion the flat samples were rubbed with cotton swabs. Testing was conducted at room temperature.
SUBJECTIVE OBSERVATION OF VISUAL CHANGE
CHEMICAL REAGENT
APPEARANCE OF WIRE MARKER
R4300
Methyl Ethyl Ketone
Severe unwrap, topcoat dissolved
Topcoat dissolved, print removed when rubbed
1,1,1-Trichloroethane
Severe unwrap, topcoat dissolved
Topcoat dissolved, print removed when rubbed
Isopropyl Alcohol
Moderate unwrap
No visible effect w/o rub, moderate smear when rubbed
Gasoline
Moderate unwrap, topcoat dissolved, slight discoloring
No visible effect w/o rub, severe print removal when rubbed
JP-8 Jet Fuel
Slight unwrap
No visible effect w/o rub, slight print smear when rubbed
Mineral Spirits
Slight unwrap
No visible effect w/o rub, slight print smear when rubbed
SAE 20 WT Oil
No visible effect to wire wrap, slight material discoloring
No visible effect w/o rub, slight print smear when rubbed
Mil 5606 Oil
No visible effect to wire wrap, slight material discoloring
No visible effect w/o rub, slight print smear when rubbed
Rust Veto® 377
No visible effect to wire wrap, slight material discoloring
No visible effect w/o rub, moderate print smear when rubbed
Speedi Kut Cutting Oil 332
No visible effect to wire wrap, slight material discoloring
No visible effect w/o rub, slight print smear when rubbed
Super Agitene®
No visible effect
No visible effect w/o rub, moderate print smear when rubbed
Skydrol® 500B-4
Slight unwrap, topcoat and adhesive softened
Severe print fade w/o rub, topcoat and print removed when rubbed
Deionized Water
No visible effect
No visible effect with or without rub
3% Alconox® Detergent
No visible effect
No visible effect with or without rub
5% Salt Water Solution
No visible effect
No visible effect with or without rub
10% Sodium Hydroxide Solution
No visible effect
Severe print fade w/o rub, complete print removal when rubbed
10% Sulfuric Acid Solution
No visible effect
No visible effect with or without rub
Northwoods™ Buzz Saw
Citrus Degreaser
No visible effect
No visible effect w/o rub, severe print smear when rubbed
Product testing, customer feedback, and history of similar products, support a customer
performance expectation of at least
two years from the date of receipt
for this product as long as this product is stored in its original packaging in an environment
below 80 degrees F and 60% RH
. We are confident that our product will perform well beyond this time frame. However, it remains the responsibility of the user to assess the risk of using such product. We encourage customers to develop functional testing protocols that will qualify a product's fitness for use, in their actual applications.
Trademarks:
Alconox® is a registered trademark of Alconox Co.
BradyPrinter™ is a trademark of Brady Worldwide, Inc.
Northwoods™ is a trademark of the Superior Chemical Corporation.
Polyken™ is a trademark of Testing Machines Inc.
Rust Veto® is a registered trademark of the E.F. Houghton & Co.
Skydrol® is a registered trademark of the Monsanto Company
Sunlighter™ is a trademark of the Test Lab Apparatus Company
Super Agitene® is a registered trademark of Graymills Corporation
ASTM: American Society for Testing and Materials (U.S.A.)
SAE: Society of Automotive Engineers (U.S.A.)
All S.I. Units (metric) are mathematically derived from the U.S. Conventional
Units
Note:
All values shown are averages and should not be used for specification purposes.
Test data and test results contained in this document are for general information only and shall not be relied upon by Brady customers for designs and specifications, or be relied on as meeting specified performance criteria. Customers desiring to develop specifications or performance criteria for specific product applications should contact Brady for further information.
Product compliance information is based upon information provided by suppliers of the raw materials used by Brady to manufacture this product or based on results of testing using recognized analytical methods performed by a third party, independent laboratory. As such, Brady makes no independent representations or warranties, express or implied, and assumes no liability in connection with the use of this information.
WARRANTY
Brady products are sold with the understanding that the buyers will test them in actual use and determine for themselves their adaptability to their intended uses. Brady warrants to the buyers that its products are free from defects in material and workmanship, but limits its obligation under this warranty to replacement of the product shown to Brady's satisfaction to have been defective at the time Brady sold it. This warranty does not extend to any persons obtaining the product from the buyers. This warranty is in lieu of any other warranty, express or implied, including, but not limited to, any implied warranty of merchantability or fitness for a particular purpose, and of any other obligations or liability on Brady's part. Under no circumstances will Brady be liable for any loss, damage, expense, or consequential damages of any kind arising in connection with the use, or inability to use, Brady's products.
Copyright 2007 Brady Worldwide, Inc. | All Rights Reserved
Material may not be reproduced or distributed in any form without written permission.
Brady North America | 6555 W. Good Hope Rd | Milwaukee, WI 53223 | USA | Tel: 414-358-6600 | Fax: 800-292-2289
© 2001 Brady Worldwide, Inc. All Rights Reserved
|
ISO9001